Formation of Supported Intermetallic Nanoparticles in the Pd–Zn/α-Al2O3 Catalyst Научная публикация
Журнал |
Kinetics and Catalysis
ISSN: 0023-1584 , E-ISSN: 1608-3210 |
||||
---|---|---|---|---|---|
Вых. Данные | Год: 2017, Том: 58, Номер: 4, Страницы: 471-479 Страниц : 9 DOI: 10.1134/S0023158417040127 | ||||
Ключевые слова | electron microscopy, intermetallic compound, Pd–Zn, X-ray diffraction, XPS | ||||
Авторы |
|
||||
Организации |
|
Реферат:
The structure of the Pd–Zn/α-Al2O3 catalyst, which was prepared by a joint impregnation method, was studied. According to XRD analysis data, supported intermetallic Pd–Zn particles were formed in a temperature range of 200–600°C. At 600°C, the crystal lattice of substitutional solid solution based on Pd (FCC) was finally rearranged into the tetragonal lattice of Pd–Zn. A shift of the Pd3d5/2 line in the XPS spectrum indicated the formation of the Pd–Zn intermetallic compound.
Библиографическая ссылка:
Mashkovsky I.S.
, Markov P.V.
, Bragina G.O.
, Baeva G.N.
, Bukhtiyarov A.V.
, Prosvirin I.P.
, Bukhtiyarov V.I.
, Stakheev A.Y.
Formation of Supported Intermetallic Nanoparticles in the Pd–Zn/α-Al2O3 Catalyst
Kinetics and Catalysis. 2017. V.58. N4. P.471-479. DOI: 10.1134/S0023158417040127 WOS Scopus РИНЦ CAPlus OpenAlex
Formation of Supported Intermetallic Nanoparticles in the Pd–Zn/α-Al2O3 Catalyst
Kinetics and Catalysis. 2017. V.58. N4. P.471-479. DOI: 10.1134/S0023158417040127 WOS Scopus РИНЦ CAPlus OpenAlex
Даты:
Поступила в редакцию: | 15 февр. 2017 г. |
Опубликована в печати: | 1 июл. 2017 г. |
Опубликована online: | 2 авг. 2017 г. |
Идентификаторы БД:
Web of science: | WOS:000407057400018 |
Scopus: | 2-s2.0-85026752442 |
РИНЦ: | 31064875 |
Chemical Abstracts: | 2017:1262897 |
OpenAlex: | W2740247299 |